Rice Husk Ash: Burning Procedures And Its Effect On Cementitious Properties Of Paste And Mortars

Jahaber, Mohamed Kassim (2006) Rice Husk Ash: Burning Procedures And Its Effect On Cementitious Properties Of Paste And Mortars. [Final Year Project] (Unpublished)

[thumbnail of 2008 Master - Rice Husk Ash-Burning Procedures And Its Effects On Cementitious Properties Of Past.pdf] PDF
2008 Master - Rice Husk Ash-Burning Procedures And Its Effects On Cementitious Properties Of Past.pdf

Download (3MB)

Abstract

Rice husk ash (RHA) is a waste material that needs costly disposal to avoid
environmental pollution. Nevertheless RHA has basic oxide contents that have some
cementitious properties. By and large through normal burning procedures, RHA contains
about 80%-85% amorphous Si02, which is a vital cementitious element. The focus of this
research is to establish a burning procedure to derive highly active amorphous silica from
rice husk so that its pozzolanic reactivity can be enhanced. Numerous burning procedures
have been employed for this purpose. Finally two methods of burning were established.
Even though the temperatures of burning varied between the two procedures, both were
based on the same principle of thermal combustion in three stages. In the first stage the
burning temperature was capped at 280°C, which was less than the ignition temperature
of rice husk in the presence of air. In the second stage, the temperature was maintained
between 280°C and 520°C. The presence of air is essential to oxidize the residual carbon
from the rice husk. In the third stage, the temperature was increased to 550°C but in the
absence of air. The two procedures with burning duration of 184 minutes and 176
minutes yielded silica content of 93.1 % and 94.3% respectively. The XRD Test further
confirmed that the silica was in amorphous form. The cement paste cubes containing
RHA replacements of2.5%, 5%, 7.5%, 10%, 12.5%, 15%, 17.5% & 20% were tested and
their compressive strengths were compared with control cement cubes. It was found that
the percentages replacement of 5% and 7.5% of RHA with water/cement (w/c) of 0.28
and 0.32 respectively produced higher compressive strength compared with its control
mix. The optimum w/c for cement paste cubes containing 2.5% RHA in order to get high
strength was 0.25. For other replacement ratios of 5%, 7.5%, I 0%, 12.5%, 15%, 17.5% &
20% RHA, the corresponding w/c were 0.28, 0.32, 0.32, 0.35, 0.36, 0.37, and 0.39
respectively. Test on pozzolanic activity index of RHA was carried out and compared
with RHAs that were obtained from other methods of burning. The pozzolanic activity
index of this RHA was found to have higher value compared to RHA from ferrocementincinerator. The effect of RHA on porosity of cement cubes containing RHA was also
investigated in this research and was found that RHA replacement with low w/c reduces
porosity.

Item Type: Final Year Project
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Departments / MOR / COE: Engineering > Civil
Depositing User: Users 2053 not found.
Date Deposited: 30 Sep 2013 16:55
Last Modified: 25 Jan 2017 09:46
URI: http://utpedia.utp.edu.my/id/eprint/7480

Actions (login required)

View Item
View Item