Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

Corrosion Study ofNitrided X-52 Carbon Steel in C02 Environment

Shalini, Subramaniam (2011) Corrosion Study ofNitrided X-52 Carbon Steel in C02 Environment. Universiti Teknologi PETRONAS. (Unpublished)

[img] PDF
Download (2659Kb)

Abstract

Carbon Dioxide (C02) corrosion is one the most studied fonn of corrosion in oil and gas industry. Carbon is preferred material of construction for offshore pipelines due to economy, availability and strength but this material are not corrosion resistant. As such the use of carbon steel is usually implemented with the corrosion control such as corrosion allowance, corrosion inhibitor and coating. Since corrosion involves interaction between metal surface and the environment, surface alteration by surface hardening method such as nitriding could protect the metal from corrosion. The objective of the project is to study the performance of different nitrided carbon steel based on 450°C, 480°C and 520°C in C02 environment. The corrosion rates of the nitrided samples were investigated at pH 3 and pH 4 by linear polarization resistance and electrochemical impedance spectroscopy. At ph 4, corrosion rate of sample nitrided at 450°C and 480°C decreases by 30%. However the corrosion rate increases by 50% for sample nitrided at 520°C. This may be due to the poor surface preparation of the sample and uneven nitride layer fails to protect the sample. At pH 3, the corrosion rates of nitrided samples at 480°C and 520°C were higher than untreated sample by 3% for sample nitrided at 480°C and by 70% for sample nitrided at 520°C. For the sample nitrided at 450°C, the corrosion rate was similar as the untreated sample. The slight decrease and increase in the corrosion rate at pH 3 indicate that the presence of nitriding layer was detrimental. This negative effect can be linked to porous nitriding layer that lead to galvanic coupling between the nitriding layer and bare metal. Further studies need to be conducted to confirm this possibility.

Item Type: Final Year Project
Academic Subject : Academic Department - Mechanical Engineering - Materials - Engineering materials - Polymers - Polymerisation
Subject: T Technology > TJ Mechanical engineering and machinery
Divisions: Engineering > Mechanical
Depositing User: Users 2053 not found.
Date Deposited: 08 Nov 2013 09:40
Last Modified: 25 Jan 2017 09:42
URI: http://utpedia.utp.edu.my/id/eprint/10300