Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

DURABILITY ASPECTS AND MECHANICAL PROPERTIES OF ECC CONTAINING NANO SILICA PARTICLES

ZULKEFLI, MOHD ZULKHAIRI (2014) DURABILITY ASPECTS AND MECHANICAL PROPERTIES OF ECC CONTAINING NANO SILICA PARTICLES. IRC, Universiti Teknologi PETRONAS. (Unpublished)

[img]
Preview
PDF
Download (2291Kb) | Preview

Abstract

In this study, the properties of Engineered Cementitious Composites (ECC) with the addition of Nano Silica is investigated when test on chloride ion penetration, mercury intrusion porosimetry (MIP), flexural strength (four point load bending) and compressive strength. Based on 20 different mix proportions with PVA Fiber up to 2% and Nano Silica up to 3% is use to be molded with different size such cylinder with diameter 100 mm, beam with size of 0.25mm x 0.50mm x 508mm and cube with size of 50mm x 50mm x 50mm . The mixing process based on standard procedure given. The specimen are place on curing tank for water cured for 28 days. After that, durability aspect and mechanical properties of ECC will be determine through several test. Based on the durability test on chloride ion penetration, through charge passed in term of coulomb in term of chloride permeability, the charge passed decreased with the increase of Nano silica content in ECC. But, difference with adding of PVA fiber content in ECC may increase chloride permeability the result on chloride ion penetration showed from very low to low chloride permeability of all specimen.

Item Type: Final Year Project
Academic Subject : Academic Department - Civil Engineering - Water and environment - Environmental - Wastewater treatment
Subject: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Engineering > Civil
Depositing User: Ahmad Suhairi Mohamed Lazim
Date Deposited: 30 Sep 2015 11:17
Last Modified: 25 Jan 2017 09:36
URI: http://utpedia.utp.edu.my/id/eprint/15634

Actions (login required)

View Item View Item

Document Downloads

More statistics for this item...