Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

Hot Corrosion Behavior of Thermal Spray Coating

Masipa, Karabo (2015) Hot Corrosion Behavior of Thermal Spray Coating. IRC, Universiti Teknologi PETRONAS. (Unpublished)

[img]
Preview
PDF
Download (1746Kb) | Preview

Abstract

Austenitic stainless steel AISI 304 and Boiler steels (such as P11, P22, P12) find their largest application in the manufacturing industry. These are preferred because of their superior mechanical strength, surface stability, creep and fatigue resistance. However, they are highly susceptible to hot corrosion. Therefore, surface engineering imparts hot corrosion resistance properties in high temperature corrosive environments. In the present study, Cr3C2-25NiCr coating was deposited on the substrate 304SS by High Velocity Oxygen Fuel (HVOF) technique in order to investigate the behavior of the Cr3C2-NiCr thermal spray coating. The bare specimens were boilier steel alloys P11, P12 and P22. Hot corrosion test was conducted on bare and coated specimens in 40%K2SO4 -40%Na2SO4 -10%NaCl -10%KCl environment at 900 °C for 10 cycles. Corrosion kinetics was monitored using weight gain measurements. Characterization of corrosion products was carried out by scanning electron microscope with energy-dispersive x-ray spectroscopy (SEM/EDS) technique. The observed corrosion resistance of the Cr3C2-NiCr coating can be attributed to the formation of protective oxide scale Cr2O3. The corrosion mechanism of the coating is discussed.

Item Type: Final Year Project
Academic Subject : Academic Department - Mechanical Engineering - Petroleum
Subject: T Technology > TJ Mechanical engineering and machinery
Divisions: Engineering > Mechanical
Depositing User: Ahmad Suhairi Mohamed Lazim
Date Deposited: 16 Dec 2015 08:59
Last Modified: 25 Jan 2017 09:36
URI: http://utpedia.utp.edu.my/id/eprint/16221

Actions (login required)

View Item View Item

Document Downloads

More statistics for this item...