Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

Repeating Weld Repair’s Effect on Microstructure and Mechanical Properties of Weld Metal

Anis Rafie bin Ahmat Rmadani, Anis Rafie (2008) Repeating Weld Repair’s Effect on Microstructure and Mechanical Properties of Weld Metal. Universiti Teknologi Petronas, Sri Iskandar,Tronoh,Perak. (Unpublished)

[img]
Preview
PDF
Download (6Kb) | Preview
[img]
Preview
PDF
Download (56Kb) | Preview

Abstract

welding standards, there is not limit on the number of times that welding repair can be done on the same spot. However, it is widely practiced to limit the repairs to two times at the same spot. This is due to possibility of microstructure degradation as result from repeating heat input in the welding process. The purpose of this project is to study and examine the consequences of repeated weld repair; the weld repair will be repeated four times on the same spot. These weld repairs were done on SA 516 Grade 70 plates using shielded metal arc welding (SMAW) for welding and normal grinding for gouging the defects area. The resultant properties will be based on toughness evaluation of the weld plate and microstructure degradation of the weld. The weld joint design is prepared according to the AWS and ASME standards and specifications. After the first weld, the original weld seam (OWS) will be obtained. OWS and parent material will be inspected based on the three features; microstructure behavior, mechanical properties and elements distribution. The defect spot will be gouged and weld repair will be made to obtain first weld seam repair (1WR) and this is repeated for three times. Inspection data will be recorded to compare the differences between all the five weld seams. The results show that the toughness of the weld decreases and the grain size of the microstructure on the HAZ increase as number of weld repair increases in relation with the number of weld repair. Thus, repeated weld repairs do show some degradation in terms of mechanical properties and microstructure behavior. Further study could be conducted to characterize these changes.

Item Type: Final Year Project
Subject: T Technology > TJ Mechanical engineering and machinery
Divisions: Engineering > Mechanical
Depositing User: Users 5 not found.
Date Deposited: 11 Jan 2012 12:24
Last Modified: 25 Jan 2017 09:45
URI: http://utpedia.utp.edu.my/id/eprint/634

Actions (login required)

View Item View Item

Document Downloads

More statistics for this item...