Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

Effects of Surface Roughness on the Adhesion and Corrosion Properties of Organic Coating Applied on One Surface of One Sample Set of Mild Steel

Ahmad Helmi Mohd Amin, Ahmad Helmi (2010) Effects of Surface Roughness on the Adhesion and Corrosion Properties of Organic Coating Applied on One Surface of One Sample Set of Mild Steel. Universiti Teknologi Petronas. (Unpublished)

[img]
Preview
PDF
Download (12Mb) | Preview

Abstract

This report basically discusses the research done and basic understanding of the chosen topic, which is the Effects of Surface Roughness on the Adhesion and Corrosion Properties of Organic Coating Applied on One Surface of One Sample Set of Mild Steel. One of the effected areas after performing surface preparation on any metal surface is the surface roughness. The samples for this study are mild steel. Three samples with different surface roughness were prepared. ASTM B 117-90 Salt Spray (Fog) test is carried out in order to study the corrosion behavior and performance in accelerated environment. The adhesion behavior was determined by performing scratch test on the coated surface after underwent the accelerated corrosive environment while the corrosion performance was determined by visual inspection. In this study, oil modified alkyd-based enamel coating is selected as the test sample.

Item Type: Final Year Project
Subject: T Technology > TJ Mechanical engineering and machinery
Divisions: Engineering > Mechanical
Depositing User: Users 5 not found.
Date Deposited: 11 Jan 2012 12:23
Last Modified: 25 Jan 2017 09:43
URI: http://utpedia.utp.edu.my/id/eprint/1476

Actions (login required)

View Item View Item

Document Downloads

More statistics for this item...