Browse content of UTPedia using Year, Subject, Department and Author and Search for required document using Searching facilities included in UTPedia. UTPedia with full text are accessible for all registered users, whereas only the physical information and metadata can be retrieved by public users. UTPedia collaborating and connecting peoples with university’s intellectual works from anywhere.

Disclaimer - Universiti Teknologi PETRONAS shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.Best viewed using Mozilla Firefox 3 or IE 7 with resolution 1024 x 768.

Wear investigation of elastically similar sliding bodies material

Muhamad Muhaidi bin Mazlan, Muhamad Muhaidi (2011) Wear investigation of elastically similar sliding bodies material. Universiti Teknologi Petronas, Sri Iskandar, Tronoh, Perak. (Unpublished)

[img]
Preview
PDF
Download (2270Kb) | Preview

Abstract

From the practical point of view to obtain the friction and wear characteristic of materials used in machinery, various types of wear testing machines have been developed and deployed. To obtain useful data for practical application, it is desirable that the investigation is carried out by a full scale wear testing apparatus having approximately similar contact conditions. There are two parameters in the wear testing machines, such as configuration of contact surface and form of the relative motion between test specimens. Thus, in this report, the effect of unidirectional sliding friction in linear sliding direction between contacting pair and friction obtained test results are investigated. The reciprocating pin-on-flat experimental technique of similar specimen’s material was modified to obtain the test results desired. The microscopic structures of the pin specimen were varied due to frictional and wear properties. Pressure distribution using selected formula during normal condition and the wear effect on the leading and trailing edge due to the movement of pin specimen were varied due to the load and number of cycles applied. Comparison between theoretical wear depth and experimental result been analyzed.

Item Type: Final Year Project
Subject: T Technology > TJ Mechanical engineering and machinery
Divisions: Engineering > Mechanical
Depositing User: Users 5 not found.
Date Deposited: 21 May 2012 11:45
Last Modified: 25 Jan 2017 09:41
URI: http://utpedia.utp.edu.my/id/eprint/2703

Actions (login required)

View Item View Item

Document Downloads

More statistics for this item...