Comparative Study on the Mechanical and Physical Properties of Un-nitriding and Nitriding of 430 Ferritic Stainless Steel

Haris, farhana (2013) Comparative Study on the Mechanical and Physical Properties of Un-nitriding and Nitriding of 430 Ferritic Stainless Steel. [Final Year Project] (Unpublished)

[thumbnail of finalreport Farhana bt Haris 13061.pdf]
Preview
PDF
finalreport Farhana bt Haris 13061.pdf

Download (1MB) | Preview

Abstract

This study compares the mechanical and physical properties of un-nitriding and nitriding of 430 ferritic stainless steel. The 430 ferritic stainless steel samples are nitrided via gas nitriding at high temperature of 1200oC for 4 hours in purified nitrogen. Another part of the samples is nitride and quenched at the same time. The two samples were compared to the as received one. Martensite layer can be seen on the surface layer of the nitride samples while the nitride and quenched samples resulted in martensite and austenite phase. The hardness of the nitrided 430 ferritic stainless steel is higher than the as –received ferritic stainless steel. The nitride and quenched stainless steel sample shows a slightly higher in hardness than the nitride only. Thus, the nitriding process enhances the mechanical properties of the 430 ferritic stainless steel.
TABLE

Item Type: Final Year Project
Subjects: T Technology > TJ Mechanical engineering and machinery
Departments / MOR / COE: Engineering > Mechanical
Depositing User: Users 2053 not found.
Date Deposited: 01 Apr 2014 16:05
Last Modified: 25 Jan 2017 09:38
URI: http://utpedia.utp.edu.my/id/eprint/13691

Actions (login required)

View Item
View Item